| Adflex KS311P is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell’s proprietary Catalloy process technology. It is suitable for extrusion as well as injection molding and blow molding applications, including mechanical and decorative automotive parts requiring elastomeric type properties, like molded-in color automotive exterior components. The product is in fact used by our customers for applications with paintable and weatherable requirements, such as injection molded fascias, claddings, bumper covers, body panels, step pads, and air deflectors. It is also used as a component in compounded materials for a wide range of industrial applications. The grade is available in natural pellet form. For regulatory compliance information see Adflex KS311P Product Stewardship Bulletin (PSB).&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Good surface appearance,Sprayable,low-temperature impact resistance,Good coloring |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.5 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 46 | ISO 868 | |
| tensile strength | |||
| Fracture, 23 ℃ | 19.0 | MPa | ISO 527-2/50 |
| Yield, 23 ℃ | 14.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 800 | % | ISO 527-2/50 |
| Yield, 23 ℃ | 14 | % | ISO 527-2/50 |
| Bending modulus | |||
| String, 23 ℃ | 530 | MPa | ISO 178 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 103 | kN/m | ASTM D624 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40 ℃, localized fracture | 4.0 | kJ/m² | ISO 180-1A |
| 23 ℃, localized fracture | 49 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -40℃，3.20 mm，Energy at Peak Load，Ductile Failure | 26.0 | J | ASTM D3763 |
| 23℃，3.20 mm，Energy at Peak Load，Ductile Failure | 14.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 55.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 112 | ℃ | ISO 306/A50 |
| Melting temperature | 147 | ℃ | ISO 11357-3 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 21.7 ft/sec |
| 3. 7.22 ft/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |