| Supplier | Kolon |
| Generic | TPE |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Filling material content | |||
| 230 ℃,2.16kg | 29 | g/10min | ASTM D1238 |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Shrinkage rate | 1.1~1.2 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.5 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shaw’s D | 56 | ASTM D2240 | |
| tensile strength | |||
| 3.20 mm，200 mm/min | 15 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm, 200 mm/min | 580 | % | ASTM D638 |
| Bending modulus | |||
| 200 mm/min，3.20 mm | 163 | MPa | ASTM D790 |
| bending strength | |||
| 200 mm/min，3.2 mm | 10 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃，6.4mm | NB | J/m | ASTM D256 |
| 23℃，6.4mm | NB | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | |||
| 20 ℃/min | 195 | ℃ | ASTM D3418 |
| Vicat Softening Temp | |||
| A50 | 172 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 100~110 | ℃ | |
| Drying time | 3~8 | hr | |
| Control moisture content | ≤ 0.1 | % | |
| Mold temperature | 20~40 | ℃ | |
| Nozzle temperature | 210~220 | ℃ | |
| Front temperature of material barrel | 210~220 | ℃ | |
| Temperature in the middle of the barrel | 200~220 | ℃ | |
| Temperature at the rear of the barrel | 180~190 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |