| A conductive PPE/PA blend designed to have improved surface appearance and elevated heat resistance for powder coating. The material is suitable for injection molding. The material is only available in black.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS+PA |
| Material Status | Commercial: Negative |
| Features | Good surface appearance,Conductive,High Heat Resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 25 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.0 to 1.3 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2810 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 65.0 | MPa | ASTM D638 |
| fracture | 64.0 | MPa | ASTM D638 |
| fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 3.0 | % | ASTM D638 |
| yield | 3.0 | % | ISO 527-2/50 |
| fracture | 4.0 | % | ASTM D638 |
| fracture | 4.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2890 | MPa | ASTM D790 |
| — | 2480 | MPa | ISO 178 |
| bending strength | |||
| — | 103 | MPa | ISO 178 |
| Yield, 50 mm span | 109 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 50 | J/m | ASTM D256 |
| 23℃ | 74 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 4.00 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 188 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 185 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| B50 | 197 | ℃ | ASTM D1525 9 , ISO 306/B50 9 |
| B120 | 196 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.6E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 8.1E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.8E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 8.6E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+3 to 1.0E+4 | ohms·cm | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 93 to 107 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 mm |
| 8. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |