Arak LLDPE LL0209AA / LL0209KJ

About
LL0209AA & LL0209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer. LL0209AA & LL0209KJ are suitable for general purpose films, neat or in lean blends with LDPE and other ethylene polymers. Lean blends applications include sacks of all types, FFS and agricultural films. In lean blends they offer the following advantages: Greater draw down. Improved hot-tack and lower seal shrinkage. Better tear resistance. Higher tensile stress and elongation at break. LL0209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. LL0209AA & LL0209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight. Recommended melt temperature for extrusion is about 180°C – 225°C. * LL0209AA & LL0209KJ are suitable for food contact.&&

About

LL0209AA & LL0209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer. LL0209AA & LL0209KJ are suitable for general purpose films, neat or in lean blends with LDPE and other ethylene polymers. Lean blends applications include sacks of all types, FFS and agricultural films. In lean blends they offer the following advantages: Greater draw down. Improved hot-tack and lower seal shrinkage. Better tear resistance. Higher tensile stress and elongation at break. LL0209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. LL0209AA & LL0209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight. Recommended melt temperature for extrusion is about 180°C – 225°C. * LL0209AA & LL0209KJ are suitable for food contact.&&

Product Description
Supplier	Arak
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Smoothness,Good dissection,Food contact compliance,Thermal viscous strength,Good Tensile Strength,Good tear strength,Copolymer,Butylene copolymer
Availabilitys	Africa & Middle East
Process Methods	Film extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.920	g/cm³	ASTM D2838
Melt Flow Rate
190℃，2.16kg	0.90	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	38	µm
film thickness	35-100 µm
tensile strength			ASTM D882
MD, yield	10.5	MPa	ASTM D882
TD, yield	11.0	MPa	ASTM D882
MD, fracture	41.0	MPa	ASTM D882
TD, fracture	32.0	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture	620	%	ASTM D882
TD, fracture	840	%	ASTM D882
Drop hammer impact	150	g	ASTM D1709
Elmandorf tear strength			ASTM D1922
MD：25 µm	150	g	ASTM D1922
TD：25 µm	370	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	100	℃	ASTM D1525

optical performance	Nominal value	Unit	Test method
gloss
45°	56		ASTM D2457
Haze	10	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Drying temperature	< 50	°C
Melt temperature	180 to 225	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.