Amodel® LF-1630 L NT-7

About
Amodel® LF-1630 L NT-7 is 30% long carbon fiber reinforced, easy-flowing PPA which can be processed on most injection molding machines. This material achieves extremely high mechanical and thermal properties, in combination with ease of processing and fast cycle times. It exhibits high strength, stiffness and impact strength at high temperatures; excellent creep and fatigue resistance; isotropic mechanical properties and reduced anisotropic shrinkage; high shear strength and high burst pressure; and an excellent surface finish.&&

About

Amodel® LF-1630 L NT-7 is 30% long carbon fiber reinforced, easy-flowing PPA which can be processed on most injection molding machines. This material achieves extremely high mechanical and thermal properties, in combination with ease of processing and fast cycle times. It exhibits high strength, stiffness and impact strength at high temperatures; excellent creep and fatigue resistance; isotropic mechanical properties and reduced anisotropic shrinkage; high shear strength and high burst pressure; and an excellent surface finish.&&

Product Description
Supplier	Solvay
Generic	PPA
Material Status	Commercial: Negative
Features	Good Rigidity,Low CLTE,Low warping,Good flexibility,High impact resistance,Fatigue resistance,Good Tensile Strength,Insulation
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.30	g/cm³	ISO 1183
Shrinkage rate
MD	0.25	%	Internal Method
Water absorption rate
Equilibrium, 23 ℃, 50% RH	0.80	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	26000	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	320	MPa	ISO 527-2
Tensile strain
fracture	1.5	%	ISO 527-2
Bending modulus
23℃	24500	MPa	ISO 178
bending strength
23℃	440	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	12	kJ/m²	ISO 179
Charpy Unnotch Impact strength
23℃	55	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	300	℃	ISO 75-2/B
1.8 MPa, unannealed	285	℃	ISO 75-2/A

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	100	ohms/sq	ASTM D257

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.080	%
Proposed maximum recycled material ratio	20	%
Barrel rear temperature	320 to 340	°C
Barrel middle temperature	320 to 335	°C
Barrel front temperature	320 to 335	°C
Nozzle temperature	325 to 340	°C
Processing (melt) temperature	< 340	°C
Mold temperature	135 to 165	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.