| HIPLEX® TR 144, copolymer of ethylene and hexene is tailored for blown film production. Extraordinary melt toughness made possible to get film down to 0.006 mm thickness. Extruded film has high impact resistance, good tear strength, excellent antiblock and good barrier properties, low gel content and excellent sealing and printing properties. Application: HIPLEX® TR-144 is suitable for production of composite films, carrier bags and other kinds of packaging. It is also recommended for blow moulding of small and medium size containers. HIPLEX® TR-144 has Health Certificate issued by Institute for Health Protection of Serbia. Also, HIPLEX® TR-144 has Statement of Conformity, which declares product’s conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good heat sealing,High impact resistance,Good Printability,High anti-blocking,Low speed solidification point,Food contact compliance,Good melt strength,Good tear strength,Copolymer,Block resin,Hexene copolymers |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.947 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.18 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Condition B, F50 | > 1000 | hr | ISO 22088 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m | 24.0 | MPa | |
| TD, yield, 25 µ m | 19.0 | MPa | |
| MD, fracture, 25 µ m | 40.0 | MPa | |
| TD, fracture, 25 µ m | 32.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| fracture | 900 | % | ISO 527-2 |
| MD, fracture, 25 µ m | 550 | % | |
| TD, fracture, 25 µ m | 690 | % | |
| Drop hammer impact | |||
| 25 µm | 80 | g | ASTM D1709 |
| tear strength | ASTM D1922 | ||
| MD，25 µm | 27.0 | kN/m | |
| TD，25 µm | 270.3 | kN/m |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 无断裂 | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 124 | ℃ | ISO 306 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blowing molding temperature | 195 to 220 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 64 | ISO 868 | |
| tensile strength | ISO 527-2 | ||
| yield | 21.0 | MPa | |
| fracture | 32.0 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 3. Blow-up ratio: 3.5-5 : 1, Neck height: 6-10 times die diameter |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |