| 15% GF reinforced PBT/ASA, High Flow version&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS+PBT |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Notched Impact Strength | ISO 179/2C | ||
| Charpy Unnotch Impact strength | ISO 179/2U | ||
| 23℃ | 30 | kJ/m² | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 4.0 | kJ/m² | |
| 23℃ | 4.0 | kJ/m² | |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 20 | kJ/m² | |
| 23℃ | 28 | kJ/m² | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | 204 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64 mm span | 152 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 215 | ℃ | ISO 306/A50 |
| B50 | 157 | ℃ | ISO 306 |
| B120 | 159 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Filler | 15 | % | ASTM D229 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 | |
| Ball hardness | |||
| H358/30 | 160 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 5300 | MPa | ASTM D638 |
| — | 5400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 85.0 | MPa | ASTM D638 |
| yield | 85.0 | MPa | ISO 527-2/5 |
| fracture | 85.0 | MPa | ASTM D638 |
| fracture | 85.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 3.0 | % | ASTM D638 |
| yield | 3.0 | % | ISO 527-2/5 |
| fracture | 3.0 | % | ASTM D638 |
| fracture | 3.0 | % | ISO 527-2/5 |
| Bending modulus | 4800 | MPa | ISO 178 |
| bending strength | 120 | MPa | ISO 178 |
| Fracture bending strain | 3.0 | % | ISO 178 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume Rate | |||
| 250℃，5 kg | 40.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.20 to 0.60 | % | Internal Method |
| Apparent viscosity of melt | |||
| 280℃，1500 sec^-1 | 55.0 | Pa·s | ISO 11443 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.20 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.079 in/min |
| 6. Break |
| 7. 2 mm/min |
| 8. 80*10*4 |
| 9. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |