| Clariant Nylon 6/6 PA-113G33C is a Polyamide 66 (Nylon 66) material filled with 33% glass fiber. It is available in North America for injection molding. Important attributes of Clariant Nylon 6/6 PA-113G33C are: Flame Rated Heat Stabilizer Lubricated Typical application of Clariant Nylon 6/6 PA-113G33C: Wire & Cable&& |
| Product Description | |
|---|---|
| Supplier | Clariant |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Lubricating,Heat Stabilized,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.60 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 96 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 260 | ℃ | |
| 1.8 MPa, unannealed | 246 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 19 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 97 | ||
| R-level | 122 | ||
| tensile strength | 172 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 9650 | MPa | ASTM D790 |
| bending strength | 262 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79.4 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 266 to 293 | °C | |
| Barrel middle temperature | 266 to 293 | °C | |
| Barrel front temperature | 266 to 293 | °C | |
| Processing (melt) temperature | 266 to 288 | °C | |
| Melt temperature (target) | 274 | °C | |
| Mold temperature | 65.6 to 93.3 | °C | |
| Injection speed | 快速 | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Cushion | 3.18 to 6.35 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |