| About |
|---|
| ELITE 5811 is an extrusion coating resin. Main Characteristics: Suitable for processing on conventional hardware Extrusion coating resin Low neck-in Good heat resistance Enhanced water vapor barrier Extra toughness High performance sealant Complies with: EU, No 10/2011 U.S. FDA 21 CFR 177.1520 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EPE |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.919 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 8.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 307 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-3 | ||
| fracture | 21.2 | MPa | ISO 527-2 |
| MD, yield | 19.3 | MPa | ISO 527-3 |
| TD, yield | 16.2 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| fracture | 720 | % | ISO 527-2 |
| MD, fracture | 540 | % | ISO 527-3 |
| TD, fracture | 610 | % | ISO 527-3 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD | 2.4 | N | ISO 6383-2 |
| TD | 3.8 | N | ISO 6383-2 |
| Initial sealing temperature | 98.0 | ℃ | Internal Method |
| Water vapor permeability | 18 | g/m²/24 hr | ASTM E96 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 102 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 124 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 260 to 320 | °C | |
| Shrinkage – 25g/m2 at 100 m/min 2 (290癈) | 84.0 | mm | |
| Pulldown – From 15g/m2 at 100 m/min 2 | 250 | m/min | |
| Min. Coating Weight – Calculated 2 | 6.0 | g/m² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| 3. – 25g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. – Temperatures at which 3 N/15mm heat seal strength is achieved. – Heat Seal Strengths measured at 0.5sec sealing time, 0.5N/mm² pressure, 5mm seal bar, cross head speed (150 mm/sec). – Kraft paper substrate |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |