| Polycarbonate for general purpose, medium-low MFI for injection molding.&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | HB,V-2 |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 13 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.80 | % | ASTM D955 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.30 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 1.1 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃，3.2mm | 150 | J/m | ASTM D256 |
| 0℃，3.2mm | 450 | J/m | ASTM D256 |
| 23℃，3.2mm | 600 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 125 | ℃ | ASTM D648 |
| Vicat Softening Temp | 147 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 25 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 9.0E-3 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 3.20 mm | HB | UL 94 | |
| 1.60 mm | V-2 | UL 94 | |
| Igniting temperature of the hot wire | 850 | ℃ | IEC 60695-2-13 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 60 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 60.0 | MPa | ASTM D638 |
| fracture | 70.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 100 | % | ASTM D638 |
| Bending modulus | 2200 | MPa | ASTM D790 |
| bending strength | |||
| fracture | 90.0 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.20 in/min |
| 4. 0.051 in/min |
| 5. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |