EQUATE PE EMDA-6147

About
EMDA-6147 is a high density polyethylene copolymer resin designed for blow molding of large size containers. Its high molecular weight and broad molecular weight distribution with a balanced density provide excellent moldability, toughness and stress-cracking resistance. The molded articles exhibit good surface attributes. EMDA-6147 is suitable for blow molding of closed head shipping containers of up to 50 liter size, fuel tanks, drums, jerry cans and other similar parts. The molded parts have smooth surfaces that can be readily treated for high quality printing. The containers may be utilized for packaging a variety of aggressive materials, such as, industrial chemicals, latex paint, printing inks and adhesives. Foodstuff can also be packaged in the containers in line with conformity of the resin with food contact regulations. EMDA-6147 is also suitable for making non-pressure “gravity” pipes for drainage and sewage applications.&&

About

EMDA-6147 is a high density polyethylene copolymer resin designed for blow molding of large size containers. Its high molecular weight and broad molecular weight distribution with a balanced density provide excellent moldability, toughness and stress-cracking resistance. The molded articles exhibit good surface attributes. EMDA-6147 is suitable for blow molding of closed head shipping containers of up to 50 liter size, fuel tanks, drums, jerry cans and other similar parts. The molded parts have smooth surfaces that can be readily treated for high quality printing. The containers may be utilized for packaging a variety of aggressive materials, such as, industrial chemicals, latex paint, printing inks and adhesives. Foodstuff can also be packaged in the containers in line with conformity of the resin with food contact regulations. EMDA-6147 is also suitable for making non-pressure “gravity” pipes for drainage and sewage applications.&&

Product Description
Generic	HDPE copolymer
Material Status	Commercial: Active
Features	Excellent Processability,Good flexibility,Good surface appearance,Wide molecular weight distribution,Good Printability,Food contact compliance,High molecular weight,Copolymer,High density,High ESCR
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.952	g/cm³	ASTM D792
Melt Flow Rate			ASTM D1238
190℃，2.16kg	0.070	g/10min	ASTM D1238
190℃，21.6kg	9.0	g/10min	ASTM D1238
ESCR(Environmental Stress Cracking Resistance)
50 ℃, 10% non-ionic surfactant, F50	1000	hr	ASTM D1693B

MECHANICAL	Nominal value	Unit	Test method
tensile strength			ASTM D638
yield	26.0	MPa	ASTM D638
fracture	35.0	MPa	ASTM D638
Tensile strain
fracture	> 750	%	ASTM D638
Bending modulus	1180	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	17.0	kJ/m²	ASTM D256

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	125	℃	ASTM D1525
Melting temperature	131	℃	Internal Method
Crystallization peak temperature
DSC	116	℃	Internal Method

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	204	°C
Barrel 2 zone temperature	204	°C
Barrel 3 zone temperature	204	°C
Barrel 4 zone temperature	204	°C
Melt temperature	210	°C
Nozzle temperature	204	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.