UNITHENE® LH614

About
UNITHENE LH614(HDPE) having high melt flow index suitable used for injection molding and the applications are thin and smart housewares, toys, etc. UNITHENE LH614 possesses good processability, high impact strength and good resistance to stress cracking, good stiffness, high hardness, good surface gloss, less warpage, low shrinkage. UNITHENE LH614 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin. Printing on items molded from UNITHENE LH614 can be easily accomplished after flame, chemical or electronic surface treatment.&&

About

UNITHENE LH614(HDPE) having high melt flow index suitable used for injection molding and the applications are thin and smart housewares, toys, etc. UNITHENE LH614 possesses good processability, high impact strength and good resistance to stress cracking, good stiffness, high hardness, good surface gloss, less warpage, low shrinkage. UNITHENE LH614 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin. Printing on items molded from UNITHENE LH614 can be easily accomplished after flame, chemical or electronic surface treatment.&&

Product Description
Supplier	USI
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,Low warping,Excellent Processability,Good surface appearance,High impact resistance,High liquidity,Good Hardness,Low contractility,High ESCR
Availabilitys	Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.962	g/cm³	ASTM D1505
Melt Flow Rate	12	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	34	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -76.0	℃	ASTM D746
Vicat Softening Temp	126	℃	ASTM D1525
Melting peak temperature	135	℃	ASTM D3418

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	69		ASTM D2240
Tensile modulus
1% cut, molded	981	MPa	ASTM D638
tensile strength			ASTM D638
yield	30.4	MPa	ASTM D638
fracture	14.7	MPa	ASTM D638
Tensile strain
fracture	170	%	ASTM D638
Bending modulus
23℃	961	MPa	ASTM D747

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.