| Flame Retardant Polystyrene (FR-HIPS) Characteristics: Ignition Resistant UL94 “V2” rated High Flow Properties Good Balance of Toughness and Rigidity Available in dark color Incorporating DBDPO Processing: Molding Gas Assist Molding Applications: TV cabinets, VCR cabinets Electrical boxes, electrical appliance parts&& |
| Product Description | |
|---|---|
| Generic | PS (IRPS) |
| Material Status | Commercial: Active |
| Features | V-2 |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 10 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23 ℃, 3.20 mm, injection molding | 25.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.20 mm, injection molding | 40 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, 3.20 mm, injection molding | 1900 | MPa | ASTM D790 |
| bending strength | |||
| 23 ℃, 3.20 mm, injection molding | 40.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, injection molded | 81.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 101 | ℃ | ASTM D1525 5 |
| Ball pressure temperature | 82.0 | ℃ | IEC 60598-1 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| 3.20 mm | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | |||
| 3.20 mm | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 23 ℃，3.20 mm，1 MHz | 2.60 | IEC 60250 | |
| Dissipation factor | |||
| 23℃，3.2 mm，1 MHz | 4.0E-4 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-2 | UL 94 | |
| Igniting temperature of the hot wire | |||
| 1.6 mm | 850 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60 to 80 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 250 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |