| Stylac™ NF920 is an Acrylonitrile Chlorinated Polyethylene Styrene (ACS) product. It is available in Africa & Middle East, Asia Pacific, or Europe. Characteristics include: Flame Rated Flame Retardant&& |
| Product Description | |
|---|---|
| Supplier | Asahi Kasei |
| Generic | ACS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Halogenated,V-0,5VA |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 59 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，10 kg | 54.5 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.6 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 74.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 88.0 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 to 1.0E-4 | 1/℃ | ASTM D696 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| Ball pressure test | 80 | ℃ | EMAC |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm | 5VA | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 101 | ISO 2039-2 | |
| tensile strength | |||
| yield | 44.1 | MPa | ISO 527-2/50 |
| Bending modulus | 2550 | MPa | ISO 178 |
| bending strength | 69.8 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |