| About |
|---|
| Staramide BST03 is an Impact Modified Polyamide 6 Injection Molding Resin&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 1.4 to 1.8 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | > 100 | kJ/m² | ISO 179/1eU |
| 23℃ | > 100 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | 25 | kJ/m² | ISO 180-1A |
| 23℃ | 35 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 100 mm span | 65.0 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| B120 | 180 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~60℃ | 9.5E-5 | 1/℃ | ISO 11359-2 |
| TD：23~60℃ | 1.2E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | IEC 60112 | ||
| CTI | 600 | V | IEC 60112 |
| Solution B | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm, E2P measurement | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 110 | ISO 2039-2 | |
| Tensile modulus | 2500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.1 | % | ASTM D638 |
| fracture | > 100 | % | ISO 527-2/50 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 220 to 230 | °C | |
| Barrel middle temperature | 230 to 240 | °C | |
| Barrel front temperature | 240 to 250 | °C | |
| Processing (melt) temperature | 240 to 250 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 120x10x4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |