| About |
|---|
| UNITIKA Nylon 6 A1030GFL is a Polyamide 6 (Nylon 6) material filled with 30% glass fabric. It is available in Asia Pacific or North America. Primary attribute of UNITIKA Nylon 6 A1030GFL: Flame Rated. Typical applications include: Automotive Construction Applications Housings&& |
| Product Description | |
|---|---|
| Supplier | UNITIKA |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific,North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Water Absorption | |||
| 23℃，50% r.h. | 2.0 | % | ISO 62 |
| Molding shrinkage | |||
| Flowing flow | 0.2 | % | Internal Method |
| Vertical direction | 0.7 | % | Internal Method |
| Melt Volume Rate | |||
| 275℃，5kg | 55 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Yield yld, dry dry dry | 170 | MPa | ISO 527-2 |
| Broken BRK, dry dry | 170 | MPa | ISO 527-2 |
| Yield yld, wet cond | 110 | MPa | ISO 527-2 |
| Broken BRK, wet Cond | 110 | MPa | ISO 527-2 |
| Tensile Modulus | |||
| Dry | 9900 | MPa | ISO 527 |
| Wet Cond | 6000 | MPa | ISO 527 |
| Tensile Elongation | |||
| Yield yld, dry dry dry | 3 | % | ISO 527-2 |
| Broken BRK, dry dry | 3 | % | ISO 527-2 |
| Yield yld, wet cond | 5 | % | ISO 527-2 |
| Broken BRK, wet Cond | 5 | % | ISO 527-2 |
| Flexural Strength | |||
| Dry | 260 | MPa | ISO 178 |
| Wet Cond | 160 | MPa | ISO 178 |
| Flexural Modulus | |||
| Dry | 8500 | MPa | ISO 178 |
| Wet Cond | 5000 | MPa | ISO 178 |
| Rockwell hardness | |||
| Dry | 120 | ISO 2039-2 | |
| Wet Cond | 107 | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| Dry | 70 | kJ/m² | ISO 179/1eU |
| Wet Cond | 85 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| Dry | 13 | kJ/m² | ISO 179/1eA |
| Wet Cond | 19 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Coeff. of linear thermal expansion | |||
| Dry | 0.3 | ×10-4/℃ | ISO 11359-2 |
| Hot deformation temperature HDT | |||
| Dry | 205 | ℃ | ISO 75-1/-2 |
| Wet Cond | 220 | ℃ | ISO 75-1/-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | 1E13 | ohm·m | IEC 62631-3-1 |
| Electric strength | 42 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.3 | IEC 62631-3-1 | |
| Dissipation Factor | 0.022 | IEC 62631-3-1 | |
| Compared Tracking Index | 550 | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.75 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Cylinder temperature | 250-270 | ℃ | |
| Mold Temperature | 80-120 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |