| LNP™ LUBRICOMP™ YL003C compound LUBRICOMP* YL003C is a compound based on Polyester Elastomer resin containing 15% PTFE. Added features of this grade include: Clean Compound System, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound YL-4030 CCS Product Reorder name: YL003C&&LNP™ LUBRICOMP™ YL003C compound LUBRICOMP* YL-4030 CCS is a PTFE Lubricated Compound based on Polyester Elastomer resin which has low ionic and low outgassing performance for the Semicon and Internal Hard Disk Drive applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | TPEE |
| Material Status | Commercial: Active |
| Features | Low (to None) Ion Content,Low odor,Lubricating,Good wear resistance,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：24 hrs | 1.7 to 1.9 | % | ASTM D955 |
| MD：24 hrs | 1.5 to 1.7 | % | ASTM D955 |
| TD：24 hrs | 1.8 | % | ISO 294-4 |
| MD：24 hrs | 1.6 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.50 | % | ISO 62 |
| 23℃，24hr | 0.20 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 56 | ASTM D2240 | |
| Tensile modulus | 280 | MPa | ASTM D638 |
| Tensile modulus | 260 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 22.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 90 | % | ASTM D638 |
| fracture | > 450 | % | ISO 527-2/50 |
| Bending modulus | 290 | MPa | ASTM D790 |
| Bending modulus | 280 | MPa | ISO 178 |
| bending strength | 19.0 | MPa | ASTM D790 |
| bending strength | 12.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 150 | J/m | ASTM D256 |
| 23℃ | 580 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| 23℃ | 23 | kJ/m² | ISO 180/1U |
| 23℃ | 48 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 57.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 6.4 mm | 54.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 88.0 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 6.4 mm | 85.0 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 1.8E-4 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 1.8E-4 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 1.1E-4 | 1/℃ | ASTM E831 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 182 to 193 | °C | |
| Barrel middle temperature | 204 to 216 | °C | |
| Barrel front temperature | 227 to 238 | °C | |
| Processing (melt) temperature | 216 to 238 | °C | |
| Mold temperature | 27 to 54 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |