| SARANEX™ 23P Coextruded Barrier Film is a multi-layer film designed for limited use protective garments. It contains Dow SARAN™ barrier resin, and is available as 2.0 mil, medium slip, natural color, TX, in widths from 10 to 62 inches (250 mm to 1570 mm). General Characteristics: Yield: 13,500 sq in./lb (19.2 m²/kg) Thickness: 2.0 mil (51 µm) Width: 10 – 62 in. (254 – 1575 mm) Color: Natural Treat: TX (untreated)&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | PVDC |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| film | Nominal value | Unit | Test method |
| film thickness | |||
| test | 51 | µm | ASTM D374 |
| film thickness | 2.0 mil (51 µ | ||
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 51 µ m | 193 | MPa | ASTM D882 |
| 2% secant, TD: 51 µ m | 221 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, fracture, 51 µ m | 24.1 | MPa | ASTM D882 |
| TD, fracture, 51 µ m | 17.2 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 51 µ m | 370 | % | ASTM D882 |
| TD, fracture, 51 µ m | 510 | % | ASTM D882 |
| Oxygen transfer rate | |||
| 23℃，50% RH，51 µm | 12 | cm³/m²/24 hr | ASTM D3985 |
| Water vapor transmittance | |||
| 38℃，90% RH，51 µm | 3.9 | g/m²/24 hr | ASTM F1249 |
| Heat sealing strength | Internal Method | ||
| MD | 540 | N/m | Internal Method |
| TD | 540 | N/m | Internal Method |
| dosage | |||
| 50.8 µm | 19.2 | m²/kg | ASTM D4321 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 1 sec preheat, 1 sec dwell, 30 psi (2.1 Bar), 350°F (177°C) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |