| LUTENE FB0300 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of heavy duty sacks and pallet shrink films. LUTENE FB0300 have the excellent mechanical properties and high stress cracking resistance make suitable for heavy duty bags and particularity bottom sealed bags. (LUTENE FB0300 contains no slip agent.) Applications: Packing of heavy products, Shrink hoods, Pallet shrink covers, all types of industrial packing&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | High ESCR |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.921 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.40 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | > 500 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tear resistance | ASTM D1922 | ||
| MD | 36.3 | MPa | ASTM D1922 |
| TD | 37.3 | MPa | ASTM D1922 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| tensile strength | ASTM D882 | ||
| MD, fracture | 23.5 | MPa | ASTM D882 |
| TD, fracture | 22.6 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 550 | % | ASTM D882 |
| TD, fracture | 650 | % | ASTM D882 |
| Drop hammer impact | 300 | g | ASTM D1709 |
| Oxygen permeability | 2000 | cm³/m²/24 hr | Internal Method |
| Water vapor permeability | 10 | g/m²/24 hr | Internal Method |
| Nitrogen transfer rate | 3500 | cm³/m²/24 hr | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 95.0 | ℃ | ASTM D1525 |
| Melting temperature | 110 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 95 | ASTM D2457 | |
| Haze | 17 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 220 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |