| About |
|---|
| Versions are available with various levels of copolymer to achieve desired levels of impact and modulus balance. Colors available meeting FDA requirements for food content applications. Compounds are offered with higher gloss. Note: Custom colors available upon request.&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | High impact resistance,Ductility,Moderate liquidity,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.4 to 2.2 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 40 | J/m | ASTM D256 |
| 23℃，3.2mm | 190 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 1400 | J/m | ASTM D256 |
| Drop hammer impact | ASTM D3029 | ||
| -30℃ | 24.4 | J | ASTM D3029 |
| 23℃ | 18.1 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 43.9 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 83.3 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 67 | ASTM D2240 | |
| tensile strength | |||
| yield | 18.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 440 | % | ASTM D638 |
| Bending modulus | |||
| tangent | 986 | MPa | ASTM D790 |
| bending strength | 30.3 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 83 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 88 | °C | |
| Drying time | 1.0 | hr | |
| Barrel rear temperature | 224 to 229 | °C | |
| Barrel middle temperature | 224 to 229 | °C | |
| Barrel front temperature | 227 to 232 | °C | |
| Nozzle temperature | 232 to 243 | °C | |
| Mold temperature | 16 to 49 | °C | |
| Injection pressure | 4.14 to 7.58 | MPa | |
| Hold pressure | 1.72 to 4.83 | MPa | |
| Back pressure | 0.517 to 1.03 | MPa | |
| Clamping force | 3.4 to 5.5 | kN/cm² | |
| Cushion | 3.18 to 6.35 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |