Premi-Glas® 2206-15 CR-SX

About
Premi-Glas® 2206-15 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant, and HVAC applications. Key Features and Benefits: Non-Halogen FR technology for regulatory compliance. Pigmentable for molded-in color; best appearance with mold texture. UL 94-5VA flame resistance at 2.3mm minimum thickness. Suitable for outdoor use in applications involving UV exposure and water immersion in accordance with UL746C (f1). File E42524. This SMC product is generally intended to be compression molded in matched metal die molds, typically at 300°F (150°C) and 500 to 1000 psi (35-65 BAR) molding pressure. Strength values may be affected by the molding process. Nominal values for polymerization shrinkage (0.0015 to 0.0025 in/in) and specific gravity (1.75 to 1.85) may be customized for individual applications. Contact your A. Schulman sales representative for specific design recommendations.&&

About

Premi-Glas® 2206-15 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant, and HVAC applications. Key Features and Benefits: Non-Halogen FR technology for regulatory compliance. Pigmentable for molded-in color; best appearance with mold texture. UL 94-5VA flame resistance at 2.3mm minimum thickness. Suitable for outdoor use in applications involving UV exposure and water immersion in accordance with UL746C (f1). File E42524. This SMC product is generally intended to be compression molded in matched metal die molds, typically at 300°F (150°C) and 500 to 1000 psi (35-65 BAR) molding pressure. Strength values may be affected by the molding process. Nominal values for polymerization shrinkage (0.0015 to 0.0025 in/in) and specific gravity (1.75 to 1.85) may be customized for individual applications. Contact your A. Schulman sales representative for specific design recommendations.&&

Product Description
Supplier	LyondellBasell
Generic	热固性聚酯
Material Status	Commercial: Active
Features	Weather resistance is good,Halogen free,Flame Characteristics,Good coloring
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.75 to 1.85	g/cm³
Shrinkage rate
MD	0.15 to 0.25	%
Weathering resistance	f1		UL 746C

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	8960	MPa	ASTM D638
tensile strength	31.0	MPa	ASTM D638
Bending modulus	8960	MPa	ASTM D790
bending strength	96.5	MPa	ASTM D790
Poisson’s ratio	0.30

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	450	J/m	ASTM D256
Impact strength of cantilever beam notch	590	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Linear coefficient of thermal expansion
TD	3.6E-5	1/℃
MD	2.7E-5	1/℃
Thermal conductivity coefficient	0.36	W/m/K
Relative temperature index
Electrical performance	130	℃	UL 746
Strength mechanical performance	130	℃	UL 746
Impact mechanical performance	130	℃	UL 746

Electrical performance	Nominal value	Unit	Test method
Dielectric strength	18	kV/mm	ASTM D149
Arc resistance	> 180	sec	ASTM D495
Compared to the leakage tracing index	600	V	ASTM D2303

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
2.20 mm	V-0 5VA		UL 94

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.