| Promyde B30 P2 U0 is a UL certified unfilled injection moulding Polyamide 6 flame retardant (Halogen free), heat stabilized. CHARACTERISTICS Promyde B30 P2 U0 is a polyamide 6 with high mechanical strength, heat stabilized, lubricated and nucleated for injection moulding. Its halogen free flame retardant system enhances its flame behavior to V0 – UL certified . APPLICATIONS Promyde B30 P2 U0 allows a fast and efficient mould filling, and an easy mould release, that combined with its excellent mechanical properties, and its flame retardant properties make it suitable for components specially used in electrical and electronics industries.&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Nucleation,Quick molding cycle,Halogen free,Good stripping performance,Flame Characteristics,Lubricating,Heat Stabilized,V-0 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 275℃，5 kg | 145 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.80 to 1.1 | % | |
| MD | 0.90 to 1.1 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 9.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.5 | % | ISO 62 |
| Viscosity number | 125 | cm³/g | ISO 307 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 3800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 85.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 3.5 | % | ISO 527-2/50 |
| Nominal tensile fracture strain | |||
| 23℃ | 9.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 3400 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 116 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 55 | kJ/m² | ISO 179/1eU |
| 23℃ | 60 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 200 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 222 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| TD：23~80℃ | 9.0E-4 | 1/℃ | ISO 11359-2 |
| MD：23~80℃ | 9.0E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric constant | |||
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.030 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1.5 mm | 775 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | < 80 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Injection speed | Moderate-Fast | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |