| Neoflon® EFEP RP-5000AS, a functionalized and onductive EFEP, was developed primarily for tubing extrusion. It can be coextruded with other resins such as polyamides directly. It has excellent processability.&& |
| Product Description | |
|---|---|
| Supplier | Daikin Fluorochemicals |
| Generic | 含氟聚合物 |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Good bond,Solvent resistance,Antistatic property,low-temperature impact resistance,Hydrocarbons |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.76 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 265℃，5.0kg | 2.0 to 8.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 29.0 to 50.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 200 to 350 | % | ASTM D638 |
| Bending modulus | 1400 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 195 | ℃ | DSC |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Permeation Resistance – Average（60℃） | 6.5 | g·mm/m²/atm/24 hr |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 260 | °C | |
| Barrel 3 zone temperature | 260 | °C | |
| Barrel 5 zone temperature | 260 | °C | |
| Connector temperature | 265 | °C | |
| Nozzle temperature | 280 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. ASTM D-7472 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |