| About |
|---|
| Description BI302 is a high impact polypropylene designed for film application. Due to ethylene-propylene rubber design, BI302 shows high impact strength. Films made from this grade provide excellent mechanical strength, thus this grade is highly suited for retort pouch film application. Characteristics High impact strength Punch resistance Transparency Applications Retort pouch, Cast film&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | PP homopolymerization |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Good Clarity,High impact resistance,Food contact compliance,Block Copolymer,Puncture Resistant |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 105 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 60 | ASTM D785 | |
| tensile strength | |||
| yield | 25.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 |
| Bending modulus | 981 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |