SABIC® HDPE CC253

About
SABIC® HDPE CC253 offers a good combination of stiffness, impact resistance, ESCR and organoleptic properties. The typical applications of this grade are mainly injection moulding and compression moulding of caps for sparkling water and carbonated soft drinks. SABIC® HDPE CC253 does not contain slip agent. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE CC253 offers a good combination of stiffness, impact resistance, ESCR and organoleptic properties. The typical applications of this grade are mainly injection moulding and compression moulding of caps for sparkling water and carbonated soft drinks. SABIC® HDPE CC253 does not contain slip agent. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,Good sensory characteristics.,High density,High ESCR
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.952	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	1.8	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
2 mm, molded into shape	1100	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	26.0	MPa
Fracture, 2 mm, molded	30.0	MPa
Tensile strain
Fracture, 2 mm, molded	> 200	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1150	MPa	ISO 178
bending strength
2 mm, molded into shape	26.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, molded	7.0	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	80.0	℃	ISO 75-2/B
Vicat Softening Temp	124	℃	ISO 306/A
Melting temperature
DSC	131	℃	ISO 11357-3
Enthalpy Change	201	J/g	ISO 11357-3

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.