| HIDEN® P300X is a High Density Polyethylene material. It is available in Asia Pacific. Important attributes of HIDEN® P300X are: Good Flexibility Heat Resistant Typical applications include: Food Contact Applications Plumbing/Piping/Potable Water&& |
| Product Description | |
|---|---|
| Supplier | YUHWA |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good flexibility,High Heat Resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.030 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| balance | < 0.010 | % | ASTM D570 |
| ESCR(Environmental Stress Cracking Resistance) | > 5000 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 24.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -80.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 124 | ℃ | ASTM D1525 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| cross-linking | > 75 | % | ISO 15875 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10% |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |