| Daelim Po1y® XP9200N is a Metallocene Linear Low Density Polyethylene product. It is available in Asia Pacific or Europe. Applications of Daelim Po1y® XP9200N include agricultural, coating applications, film, food contact applications and wrap. Characteristics include: Good Sealability Antiblock Antioxidant Clarity Good Stiffness&& |
| Product Description | |
|---|---|
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good surface appearance,Smoothness,High anti-blocking,Good melt strength,Good tear strength,Soft,Terpolymer,Low temperature heat sealing |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.5 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 30 µ m, blow molded film | 45.1 | MPa | ASTM D882 |
| MD，断裂，30 µm，吹塑薄膜 | 56.9 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 30 µ m, blow molded film | 620 | % | ASTM D882 |
| MD，断裂，30 µm，吹塑薄膜 | 580 | % | ASTM D882 |
| Drop hammer impact | |||
| 30 µ m, blow molded film | 670 | g | ASTM D1709-B |
| Sealing starting temperature | |||
| 30 µ m, blow molded film | 95.0 | ℃ | Internal Method |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | ASTM D1004 | ||
| TD，0.0300 mm | 125 | kN/m | ASTM D1004 |
| MD，0.0300 mm | 122 | kN/m | ASTM D1004 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 106 | ℃ | ASTM D1525 |
| Melting peak temperature | 116 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 30 µ m, blow molded film | 87 | ASTM D2457 | |
| Haze | |||
| 30 µ m, blow molded film | 12 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 150 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. HGT, 2.8 kg, 0.5 sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |