| Kangxi® FRPET-30GF是一种聚对苯二甲酸乙二酯(PET)产品,含有的填充物为30% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在亚太地区有供货。 Kangxi® FRPET-30GF的应用领域包括电气/电子应用、汽车行业 和 电气用具。 特性包括: 阻燃/额定火焰 Flame Retardant 耐热 高强度&& |
| Product Description | |
|---|---|
| Supplier | Kangxi |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Flame Characteristics,High Heat Resistance,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.65 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.30 | % | ASTM D955 |
| TD | 0.90 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 90 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 230 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 220 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Weathering resistance | |||
| 24 hrs，23℃ | 0.060 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | 120 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.5 | % | ASTM D638 |
| Bending modulus | 8000 | MPa | ASTM D790 |
| bending strength | 170 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 140 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 230 to 270 | °C | |
| Barrel middle temperature | 230 to 270 | °C | |
| Barrel front temperature | 230 to 270 | °C | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 80 to 110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |