| About |
|---|
| CALIBRE™ 5201-12 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIBRE 5201-12 resin is typically used in medical market applications. CALIBRE 5201-12 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics: Glass reinforced Ignition resistant Tested under ISO 10993 Applications: Medical applications Handheld surgical devices Powered medical devices Equipment housings Electrical components&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Dimensional Stability,Biocompatible,Flame Characteristics,V-2,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ASTM D792 , ISO 1183/B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 12 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | |||
| MD | 0.20 to 0.40 | % | ASTM D955 |
| MD | 0.20 to 0.40 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 110 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，3.20 mm，Total Energy | 46.3 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 148 | ℃ | ASTM D648，ISO 75-2/B |
| 1.8 MPa, unannealed | 138 | ℃ | ASTM D648，ISO 75-2/A |
| 1.8 MPa, annealed | 142 | ℃ | ASTM D648，ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 159 | ℃ | ASTM D1525 7 |
| B50 | 158 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 | |
| Tensile modulus | |||
| — | 5170 | MPa | ASTM D638 |
| — | 5170 | MPa | ISO 527-2/50 |
| tensile strength | |||
| yield | 82.7 | MPa | ASTM D638 |
| yield | 82.7 | MPa | ISO 527-2/50 |
| fracture | 82.7 | MPa | ASTM D638 |
| fracture | 82.7 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 2.6 | % | ASTM D638 |
| yield | 2.6 | % | ISO 527-2/50 |
| fracture | 3.0 | % | ASTM D638 |
| fracture | 2.6 | % | ISO 527-2/50 |
| Bending modulus | |||
| — | 4830 | MPa | ASTM D790 |
| — | 4820 | MPa | ISO 178 |
| bending strength | |||
| — | 148 | MPa | ASTM D790 |
| — | 148 | MPa | ISO 178 |
| Notes |
|---|
| 1. Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. 2.0 in/min |
| 4. Method I (3 point load), 0.079 in/min |
| 5. 0.079 in/min |
| 6. 11.1 ft/sec |
| 7. Rate A (50°C/h), Loading 2 (50 N) |
| 8. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |