| InnoPlus HD3355F is produced by slurry process, a technology licensed by Mitsui. This grade has well balance property of optical property, mechanical property and processability. The special characteristic of this grade consists of low gel content, stiffness and packing property. This grade is suitable for high quality film, produced by co-extrusion process. Typical Application : Laminated film, Laminated Tube, General purpose film for packaging.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low speed solidification point,Food contact compliance,High density |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.1 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 140 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 122 | ℃ | ASTM D1525 2 |
| Melting peak temperature | 131 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 62 | ASTM D2240 | |
| tensile strength | |||
| yield | 23.5 | MPa | |
| fracture | 36.3 | MPa | |
| Tensile strain | |||
| fracture | > 1000 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 735 | MPa | ASTM D747 |
| Bending modulus | 1080 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 170 to 190 | °C | |
| Barrel 3 zone temperature | 170 to 190 | °C | |
| Barrel 5 zone temperature | 170 to 190 | °C | |
| Nozzle temperature | 190 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |