| About |
|---|
| 33% Glass Reinforced, Heat Stabilized&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low liquidity,High impact resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，50% RH | 1.90 | % | ISO 62 |
| 23℃，24hr | 6.30 | % | ISO 62 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 210 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/Bf |
| Melting temperature | 220 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| MD | 2.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+14 | Ω.cm | IEC 60093 |
| Insulation strength | 30 | KV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 23℃ | 3.50 | 100 Hz | IEC 60250 |
| 23℃ | 3.30 | 1 MHz | IEC 60250 |
| Dissipation factor | |||
| 23℃ | 5.0E-3 | 100 Hz | IEC 60250 |
| 23℃ | 0.015 | 1 MHz | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | 0.71mm | HB | UL-94 |
| Flame retardant level | 1.50mm | HB | UL-94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70-80 | °C | |
| Drying time | 4.0-12 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 210-240 | °C | |
| Barrel middle temperature | 220-250 | °C | |
| Barrel front temperature | 230-260 | °C | |
| Nozzle temperature | 240-270 | °C | |
| Mold temperature | 40-120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |