| About |
|---|
| Adflex Q 100 F is a thermoplastic polyolefin, which is mainly used by our customers for the extrusion of blown film. It is also suitable for sheet extrusion. Adflex Q 100 F features very high softness and very low modulus. It does not contain any slip or anti-blocking agents. Adflex Q 100 F is used for the production of soft hygienic film and heavy duty film, as well as for the modification of LDPE or LLDPE to increase mechanical characteristics, puncture resistance, and to allow further downgauging. It can be easily processed on conventional LDPE or LLDPE blown film lines.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Good tear strength,Soft,low-temperature impact resistance,Puncture Resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.880 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.60 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 30 | ISO 868 | |
| Bending modulus | 100 | MPa | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-3/25 | ||
| MD, 50 µ m, blow molded film | 90.0 | MPa | ISO 527-3/25 |
| TD, 50 µ m, blow molded film | 90.0 | MPa | ISO 527-3/25 |
| tensile strength | ISO 527-3/500 | ||
| fracture | 10.0 | MPa | ISO 527-2 |
| MD, yield, 50 µ m, blow molded film | 7.50 | MPa | ISO 527-3/500 |
| TD, yield, 50 µ m, blow molded film | 7.50 | MPa | ISO 527-3/500 |
| tensile strength | ISO 527-3/500 | ||
| MD, fracture, 50 µ m, blow molded film | 40.0 | MPa | ISO 527-3/500 |
| TD, fracture, 50 µ m, blow molded film | 37.0 | MPa | ISO 527-3/500 |
| Tensile strain | ISO 527-3/500 | ||
| MD, fracture, 50 µ m, blow molded film | 1000 | % | ISO 527-3/500 |
| TD, fracture, 50 µ m, blow molded film | 1000 | % | ISO 527-3/500 |
| Tensile strain | ISO 527-3/500 | ||
| fracture | > 400 | % | ISO 527-2 |
| MD, yield, 50 µ m, blow molded film | 40 | % | ISO 527-3/500 |
| TD, yield, 50 µ m, blow molded film | 40 | % | ISO 527-3/500 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | No Break | ISO 180/1A | |
| 23℃ | No Break | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 40.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 60.0 | ℃ | ISO 306/A50 |
| Melting temperature | 140 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，50 µm | 9 | ASTM D2457 | |
| Haze | |||
| 50 µ m, cast thin film | 50 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |