| About |
|---|
| ADDILENE® J 290 M20 F is a Polypropylene Copolymer (PP Copolymer) material filled with 20% mineral. It is available in Africa & Middle East, Asia Pacific, Europe, or Latin America. Important attributes of ADDILENE® J 290 M20 F are: Flame Rated Flame Retardant Typical applications include: Electrical/Electronic Applications Industrial Applications&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Halogenated,V-0 |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 30 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | 5.5 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 62.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 151 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 165 to 168 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 43 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | > 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm, all colors | V-0 | UL 94 | |
| Igniting temperature of the hot wire | 960 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 27 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 70 | ISO 868 | |
| tensile strength | |||
| fracture | 25.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 13 | % | ISO 527-2 |
| Bending modulus | 2300 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |