| About |
|---|
| Resilience HC 8210 is a high flow, high impact resistance rigid grade offering enhanced chemical resistance for medical device housing applications. It is RoHS compliant with UL V0 and 5VA ratings.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PVC，刚硬 |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,V-0,5VA |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Spiral flow length | 112 | cm | |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256A | ||
| -18 ℃, 3.2mm, injection molding | 110 | J/m | ASTM D256-A |
| 0 ℃, 3.2mm, injection molding | 270 | J/m | ASTM D256-A |
| 23 ℃, 3.2mm, injection molding | 640 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35 mm | 72.2 | ℃ | ASTM D648 |
| 0.45 MPa, annealed, 6.35 mm | 75.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.35 mm | 68.9 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 6.35 mm | 72.8 | ℃ | ASTM D648 |
| Relative temperature index | 90.0 | ℃ | UL 746 |
| Electrical performance | 90.0 | ℃ | UL 746 |
| Impact mechanical performance | 85.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm, all colors | V-0 | UL 94 | |
| 1.50 mm, all colors | 5VA | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| CSA flame retardant rating (1.60 mm) | V-0 5VA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 79 | ASTM D2240 | |
| Tensile modulus | 2280 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 41.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 35 | % | ASTM D638 |
| Bending modulus | 2340 | MPa | ASTM D790 |
| bending strength | 66.9 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 199 to 210 | °C | |
| Notes |
|---|
| 1. All color |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. Type I, 2.0 in/min |
| 4. All Colors |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |