| BF4810 is a high density high molecular weight polyethylene copolymer resin that shows an excellent dart impact and puncture resistance, high tensile strength, good sealability and an outstanding processing performance. Applications: Retail bags; perforated rolls; repackaging; bags in general. Process: Blown Film Extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,High molecular weight,High density |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，21.6kg | 10 | g/10min | ASTM D1238 |
| 190℃，5.0kg | 0.45 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 13 µ m, blow molded film | 40.0 | MPa | ASTM D882 |
| TD, yield, 13 µ m, blow molded film | 25.0 | MPa | ASTM D882 |
| MD, fracture, 13 µ m, blow molded film | 50.0 | MPa | ASTM D882 |
| MD, yield, 13 µ m, blow molded film | 25.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 13 µ m, blow molded film | 860 | % | ASTM D882 |
| MD, fracture, 13 µ m, blow molded film | 510 | % | ASTM D882 |
| Drop hammer impact | |||
| 13 µ m, blow molded film | 140 | g | ASTM D1709 |
| tear strength | |||
| TD, 13 µ m, blow molded film | 70 | g | ASTM D1922 |
| MD, 13 µ m, blow molded film | 50 | g | ASTM D1922 |
| Sealing starting temperature | |||
| 13 µ m, blow molded film | 125 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | |||
| 12.5 µm | 70.0 | J/m | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |