| About |
|---|
| Polyamide 66, %25 glass fiber reinforced, V0 flammability&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 to 1.40 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.25 to 0.35 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | > 7.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 255 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 250 | ℃ | ISO 306/B |
| Melting temperature | |||
| DSC | 265 | ℃ | ISO 3146 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Igniting temperature of the hot wire | 960 | ℃ | VDE 0471/2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 75 to 80 | ISO 868 | |
| Tensile modulus | 5500 to 8000 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 140 to 160 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 3.0 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |