| (PC+ABS)-Blend; flame retardant; mineral filled ; Vicat/B 120 temperature = 102°C; UL recognition 94 V-0 at 1.2 mm; low warpage; improved stiffness and surface quality; for notebooks and thinwall applications |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Low warping,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 23℃ | 6300 | MPa | ISO 527-1-2 |
| Tensile stress | |||
| Yield, 23 ° C | 59.0 | MPa | |
| Fracture, 23 ° C | 52.0 | MPa | |
| Tensile strain | |||
| Yield, 23 ° C | 2.8 | % | |
| Fracture, 23 ℃ | 5.8 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 4.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 45 | kJ/m² | |
| 23℃ | 50 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 5.0 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 30 | kJ/m² | |
| 23℃ | 40 | kJ/m² | |
| Multi axial instrumented impact energy | |||
| -30°C | 2.00 | J | |
| 23°C | 13.0 | J | |
| Multi axial instrumented peak impact force | |||
| -30°C | 1100 | N | |
| 23°C | 2600 | N |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 96.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 90.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 100 | ℃ | ISO 306 |
| — | 102 | ℃ | ISO 306/B120 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-1 | ||
| 1.20 mm | V-0 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | |||
| 23℃ | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 27.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：2.0 mm | 0.30 | % | |
| TD：2.0 mm | 0.20 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.50 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | |
| Melt viscosity (260 ° C) | 230 | Pa·s | ISO 11443-A |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Drying temperature – Dry Air Dryer | 85 | °C | |
| Drying time – Dry Air Dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Suggested injection volume | 30 to 70 | % | |
| Temperature at the rear of the barrel | 240 to 260 | °C | |
| Temperature in the middle of the barrel | 250 to 280 | °C | |
| Front temperature of material barrel | 270 to 300 | °C | |
| Nozzle temperature | 270 to 300 | °C | |
| Processing (melt) temperature | 270 to 300 | °C | |
| Mold temperature | 65 to 100 | °C | |
| Back pressure | 5.00 to 10.0 | MPa | |
| Exhaust hole depth | 0.020 to 0.040 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |