| A FLEXIBLE, THERMOPLASTIC, ZERO HALOGEN, 105°C RATED, FLAME RETARDED, OLEFINIC, UV RESISTANT COMPOUND INTENDED FOR DEMANDING TELECOMMUNICATION CABLES.&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Halogen free,Flame Characteristics |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 to 1.53 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，10.0kg | 2.5 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 0.762 mm | 11.7 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 0.762 mm | 130 | % | ASTM D412 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s D | 57 to 63 | ASTM D2240 | |
| Shore D, 15 seconds | 48 to 54 | ASTM D2240 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -20.0 | ℃ | ASTM D746 |
| Hot pressure test (% Loss, 80 ℃) | 20 | % | IEC 811-3-1 |
| Temperature index | > 355 | ℃ | NES 715 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air (136 ℃, 168 hr) | -6.0 | % | UL Unspecified |
| The rate of change in ultimate elongation in air | |||
| 136℃，168 hr | -13 | % | UL Unspecified |
| The rate of change in tensile strength | |||
| 70℃，4 hr，in ASTM #2 Oil | -29 | % | UL Unspecified |
| Change in Ultimate Elongation（70℃，4 hr，in ASTM #2 Oil） | 22 | % | UL Unspecified |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | ASTM D150 | ||
| 23 ℃，1 MHz | 3.58 | ASTM D150 | |
| 23 ℃，100 MHz | 3.49 | ASTM D150 | |
| 23 ℃，200 MHz | 3.46 | ASTM D150 | |
| 23 ℃，350 MHz | 3.45 | ASTM D150 | |
| 23 ℃，600 MHz | 3.41 | ASTM D150 | |
| 23 ℃，1.00 GHz | 3.38 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 23℃，1 MHz | 0.022 | ASTM D150 | |
| 23℃，100 MHz | 0.014 | ASTM D150 | |
| 23℃，200 MHz | 0.012 | ASTM D150 | |
| 23℃，350 MHz | 0.010 | ASTM D150 | |
| 23℃，600 MHz | 8.5E-3 | ASTM D150 | |
| 23℃，1 GHz | 7.9E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | |||
| 3.18 mm | 44 | % | ASTM D2863 |
| Conductivity of acidic gas emissions | 0.380 | µS/mm | IEC 60754-2 |
| Acid gas emission pH | 5.40 | IEC 60754-2 | |
| Halogen Content | |||
| — | < 5 | mg/g | IEC 754-1 |
| — | 0 | % | MIL C-24643 |
| Smoke index | 5.35 | NES 711 | |
| toxicity | 4.60 | NES 713 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Barrel 1 zone temperature | 154 | °C | |
| Barrel 2 zone temperature | 160 | °C | |
| Barrel 3 zone temperature | 166 | °C | |
| Barrel 4 zone temperature | 171 | °C | |
| Barrel 5 zone temperature | 171 | °C | |
| Connector temperature | 177 | °C | |
| Melt temperature | 171 to 182 | °C | |
| Nozzle temperature | 177 | °C | |
| Extruder screw compression ratio | 1.5:1.0 to 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Thickness: 30 mil |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |