| About |
|---|
| Trademark PE LDVA2925.3F is a Low Density Polyethylene + EVA product. It can be processed by coextruded film and is available in North America. Applications of Trademark PE LDVA2925.3F include film, food contact applications and packaging. Characteristics include: Antiblock Clarity Food Contact Acceptable Good Stiffness High Strength&& |
| Product Description | |
|---|---|
| Generic | LDPE+EVA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Food contact compliance,Low temperature strength |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.5 | g/10min | ASTM D1238 |
| Vinyl acetate content | 2.5 | wt% | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 38 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 38 µ m, blow molded film | 141 | MPa | ASTM D882 |
| 1% secant, TD: 38 µ m, blow molded film | 169 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, fracture, 38 µ m, blow molded film | 22.1 | MPa | ASTM D882 |
| TD, fracture, 38 µ m, blow molded film | 16.9 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 38 µ m, blow molded film | 340 | % | ASTM D882 |
| TD, fracture, 38 µ m, blow molded film | 540 | % | ASTM D882 |
| Drop hammer impact | |||
| 38 µ m, blow molded film | 120 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 38 µ m, blow molded film | 210 | g | ASTM D1922 |
| TD: 38 µ m, blow molded film | 110 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 38.1 µ m, blow molded film | 76 | ASTM D2457 | |
| Haze | |||
| 38.1 µ m, blow molded film | 5.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 166 to 193 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |