| About |
|---|
| Product performance: Aluminum layer have strong adhesion, high brightness Without pinhole,without cockle. Suitable for metallic yarn slitting Application: It is extensively used in the metallic yarn and coating process.&& |
| Product Description | |
|---|---|
| Supplier | Jinxin |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good bond,Metallized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| friction coefficient | 0.48 | ASTM D1894 | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 12 | µm | ASTM D374 |
| tensile strength | ASTM D882 | ||
| MD, fracture | 235 | MPa | ASTM D882 |
| TD, fracture | 216 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 110 | % | ASTM D882 |
| TD, fracture | 140 | % | ASTM D882 |
| Oxygen permeability | |||
| 23℃ | 0.880 | cm³/m²/24 hr | ASTM D1434 |
| Water vapor permeability | 0.55 | g/m²/24 hr | ASTM E96 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 131 | ASTM D2457 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal shrinkage | ASTM D1204 | ||
| MD | 1.3 | % | ASTM D1204 |
| TD | -0.10 | % | ASTM D1204 |
| Wetting Tension | 44 | dyne/cm | ASTM D2578 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0%RH |
| 3. 150°C/30min or 190°C/5min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |