| About |
|---|
| LOCTITE STYCAST EO 7038 is a one component epoxy potting system, formulated to protect sensors used in harsh environments, such as automotive applications.&& |
| Product Description | |
|---|---|
| Supplier | Henkel |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Baking |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| THERMAL | Nominal value | Unit | Test method |
| Glass transition temperature | 140 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：40~100℃ | 3.0E-5 | 1/℃ | |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 25 ℃，50 kHz | 3.80 | ||
| 25 ℃，100 kHz | 3.70 | ||
| 100 ℃，50 kHz | 3.90 | ||
| 100 ℃，100 kHz | 3.60 | ||
| Dissipation factor | |||
| 25℃，50 kHz | 0.015 | ||
| 25℃，100 kHz | 0.013 | ||
| 100℃，50 kHz | 0.044 | ||
| 100℃，100 kHz | 0.012 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| viscosity | |||
| 25℃，Brookfield RVT | 40 | Pa·s | |
| Curing time | |||
| 140℃ | 2.0 | hr | |
| 130℃ | 3.0 | hr | |
| Gelation time | |||
| 121℃ | 16 | min | |
| storage stability | |||
| 25 ℃ | 4300 | min | |
| Storage period | |||
| 5℃ | 4 | month |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 92 | ||
| Tensile modulus | 9500 | MPa | |
| bending strength | 92.0 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Spindle 7, speed 20 rpm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |