ALCUDIA® LDPE 2605F

About
ALCUDIA® 2605F is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown film applications. This material offers easy processability and good balance of mechanical and optical properties. It contains antioxidant additives. TYPICAL APPLICATIONS Shrink films / hoods Coextruded films where good optical properties and heat resistance is required. Recommended melt temperature range from 170 to 200°C. Processing conditions should be optimised for each production line.&&

About

ALCUDIA® 2605F is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown film applications. This material offers easy processability and good balance of mechanical and optical properties. It contains antioxidant additives. TYPICAL APPLICATIONS Shrink films / hoods Coextruded films where good optical properties and heat resistance is required. Recommended melt temperature range from 170 to 200°C. Processing conditions should be optimised for each production line.&&

Product Description
Supplier	REPSOL
Generic	LDPE
Material Status	Commercial: Active
Features	Optical performance,Food contact compliance,Inoxidizability,Heat Resistance, Good
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.926	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	0.50	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
friction coefficient
Self dynamic, blow molded film	0.50		ISO 8295

film	Nominal value	Unit	Test method
film thickness
test	40	µm
tensile strength			ISO 527-3
MD, fracture, 40 µ m, blow molded film	25.0	MPa	ISO 527-3
TD, fracture, 40 µ m, blow molded film	20.0	MPa	ISO 527-3
Tensile strain			ISO 527-3
MD, fracture, 40 µ m, blow molded film	350	%	ISO 527-3
TD, fracture, 40 µ m, blow molded film	650	%	ISO 527-3
Drop hammer impact
40 µ m, blow molded film	90	g	ISO 7765-1
Elmandorf tear strength			ISO 6383-2
MD: 40 µ m, blow molded film	2.0	N	ISO 6383-2
TD: 40 µ m, blow molded film	2.0	N	ISO 6383-2

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	98.0	℃	ISO 306/A

optical performance	Nominal value	Unit	Test method
gloss
45 °, 40.0 µ m, blow molded film	75		ASTM D2457
Haze
40 µ m, blow molded film	11	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	170 to 200	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.