| Hepla ® H1100 H FR is a unreinforced Acrylonitrile Butadiene Styrene (ABS) product.Characteristics include:Characteristics include: Flame Rated,Heat Resistant,Weather Resistant. |
| Product Description | |
|---|---|
| Supplier | NFD |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,High liquidity,Low or no water absorption,Flame Characteristics,High Heat Resistance,Antistatic property |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.19 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃/5.0 kg | 2.8 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃/10.0 kg | 27 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.3-0.6 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 11.8 | kJ/m² | ISO 179 |
| 23℃ | 21.5 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃, 3.20 mm | 223 | J/m | ASTM D256 |
| -30℃ | 10.8 | kJ/m² | ISO 180/1A |
| 23℃ | 20.6 | kJ/m² | ISO 180/1A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5mm | V-0 | UL 94 | |
| 2.5mm | 5VA | UL 94 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 85 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 86 | ℃ | ISO 75-2/A |
| 1.8 MPa, annealed | 96 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 96 | ISO 75-2/A | |
| Vicat Softening Temp | |||
| 104 | ℃ | ASTM D1525 | |
| 103 | ℃ | ISO 306/A50 | |
| 96 | ℃ | ISO 306/B50 | |
| Linear coefficient of thermal expansion | |||
| MD | 8.50E-05 | cm/cm/℃ | ISO 11359-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 98 | ASTM D785 | |
| tensile strength | |||
| Yield, 6.0 mm/min | 39.5 | MPa | ASTM D638 |
| yield | 38.7 | MPa | ISO 527-2/50 |
| fracture | 29.6 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 6.0 mm/min | 29.2 | % | ASTM D638 |
| fracture | 14.5 | % | ISO 527-2/50 |
| Bending modulus | |||
| 2.8 mm/min | 2503 | MPa | ASTM D790 |
| 2.0 mm/min | 2087 | MPa | ISO 178 |
| bending strength | |||
| 2.8 mm/min | 62 | MPa | ASTM D790 |
| 2.0 mm/min | 59.4 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Processing technology | Nominal value | Unit | Test method |
| Temperature at the rear of the barrel | 180-210 | ℃ | |
| Temperature in the middle of the barrel | 190-220 | ℃ | |
| Front temperature of material barrel | 190-220 | ℃ | |
| Mold temperature | 40-70 | ℃ | |
| drying temperature | 80-85 | ℃ | |
| Drying time | 2-4 | hr | |
| Injection pressure | 4.9-7.85 | MPa | |
| Maintaining pressure | 1.96-4.9 | MPa | |
| Back pressure | 0.49-0.981 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |