PermaStat® 800 TFE 15

About
PTFE Lubricated – Permanently Anti-static – ESD Protection&&

Product Description
GenericCopolymer Polyformaldehyde
Material StatusCommercial: Negative
FeaturesElectrostatic discharge protection,Lubricating,Antistatic property
AvailabilitysAfrica & Middle East ,North America,Latin America,Asia Pacific,Europe
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.40g/cm³ASTM D792
Shrinkage rate
MD:3.2 mm1.5 to 2.0%ASTM D955
water content0.15%

MECHANICALNominal valueUnitTest method
Tensile modulus1380MPaASTM D638
tensile strength34.5MPaASTM D638
Tensile strain
yield> 10%ASTM D638
Bending modulus1520MPaASTM D790
bending strength48.3MPaASTM D790

IMPACTNominal valueUnitTest method
Impact strength of cantilever beam notch
3.2mm80J/mASTM D256
Notched impact strength of cantilever beam
3.2 mm无断裂 ASTM D4812

Electrical performanceNominal valueUnitTest method
Surface resistivity 
1.0E+9 to 9.9E+10ohmsESD STM11.11
1.0E+10 to 9.9E+11ohmsASTM D257
Volume resistivity1.0E+9 to 9.9E+10ohms·cmASTM D257
Electrostatic attenuation< 2.0secFTMS 101C 4046.1

Supplementary informationNominal valueUnitTest method
Primary Additive15%

Process Conditions
injectionNominal valueUnitTest method
Drying temperature121°C
Drying time2.0hr
Dew Point-32°C
Processing (melt) temperature177 to 204°C
Mold temperature82 to 121°C
Injection pressure68.9 to 103MPa

Notes
1. Typical properties: these are not to be construed as specifications.
2. MIL-PRF-81705D, 5kV to 50 V, 12% RH
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.