| About |
|---|
| Amodel® A-1133 NL resin is a 33% glass reinforced polyphthalamide (PPA) which is distinguished by its high-reflectivity white color. This grade features a high deflection temperature for compatibility with SMT processes, and low moisture absorption. White: A-1133 NL WH 505&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good color stability,Solvent resistance,High reflectivity,Low moisture absorption |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.54 | g/cm³ | ISO 1183/A |
| Shrinkage rate | |||
| TD | 0.60 | % | ASTM D955 |
| MD | 0.20 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.16 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 37 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 271 | ℃ | ASTM D648 |
| Melting temperature | 310 | ℃ | ASTM D570 |
| Linear coefficient of thermal expansion | |||
| TD | ASTM E831 | ||
| MD | ASTM E831 | ||
| 0 to 100 ℃ | 2.3E-5 | cm/cm/℃ | ASTM E831 |
| 160 to 249 ℃ | 1.4E-5 | cm/cm/℃ | ASTM E831 |
| 0 to 100 ℃ | 4.5E-6 | cm/cm/℃ | ASTM E831 |
| 160 to 249 ℃ | 1.0E-4 | cm/cm/℃ | ASTM E831 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12400 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 179 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.8 | % | ASTM D638 |
| Bending modulus | 11700 | MPa | ASTM D790 |
| bending strength | |||
| yield | 236 | MPa | ASTM D790 |
| Poisson’s ratio | 0.41 | ASTM E132 | |
| Rockwell hardness | |||
| R-level | 125 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.045 | % | |
| Barrel rear temperature | 304 to 318 | °C | |
| Barrel front temperature | 316 to 329 | °C | |
| Processing (melt) temperature | 321 to 343 | °C | |
| Mold temperature | 135 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |