| Features: General high gloss Applications: Products demanding for gloss: Sweeper, Wasshing machine cover etc&& |
| Product Description | |
|---|---|
| Supplier | Kumho Petrochemical |
| Material Status | Commercial: Active |
| Features | Good surface appearance,HB |
| Availabilitys | Asia Pacific,Europe,North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ASTM D1238 | ||
| 220℃，10.0kg | 40 | g/10min | ISO 1133 |
| 200℃，21.6kg | 60 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 40 | g/10min | ASTM D1238 |
| Molding shrinkage | 0.50 to 0.80 | % | ISO 294-4 |
| MD | 0.50 to 0.80 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 22 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact strength | ASTM D256 | ||
| 23℃ | 21 | kJ/m² | ISO 180-1A |
| 23℃，3.2mm | 250 | J/m | ASTM D256 |
| 23℃，6.4mm | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 86.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 81.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 92.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temperature | 96.0 | ℃ | ASTM D1525 2 |
| B50 | 96.0 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Yield yld | 46.1 | MPa | ASTM D638 |
| Yield yld | 44.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK | 20 | % | ISO 527-2 |
| Yield yld | 20 | % | ASTM D638 |
| Flexural Modulus | 2160 | MPa | ASTM D790 |
| Flexural Modulus | 23000 | MPa | ISO 178 |
| Flexural Strength | 66.0 | MPa | ISO 178 |
| Yield yld | 63.7 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 108 | ISO 2039-2 | |
| R-level | 108 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |