| About |
|---|
| Compound based on Polyamide 66 (PA 66). Heat stabilised. Glass fibres. UL94 V-0 classified, with red phosphorous. Product UL certified.&& |
| Product Description | |
|---|---|
| Supplier | LATI |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Heat Stabilized,HB,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.0 to 1.2 | % | |
| MD | 0.35 to 0.50 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | ||
| 23℃ | 8200 | MPa | |
| 60℃ | 6900 | MPa | |
| 90℃ | 4200 | MPa | |
| 120℃ | 3500 | MPa | |
| 150℃ | 2700 | MPa | |
| tensile strength | ISO 527-2 | ||
| Yield, 90 ℃ | 70.0 | MPa | |
| Yield, 120 ℃ | 50.0 | MPa | |
| Yield, 150 ℃ | 40.0 | MPa | |
| Fracture, 23 ℃ | 135 | MPa | |
| Fracture, 60 ℃ | 100 | MPa | |
| Fracture, 90 ℃ | 65.0 | MPa | |
| Fracture, 120 ℃ | 50.0 | MPa | |
| Fracture, 150 ℃ | 40.0 | MPa | |
| Tensile strain | ISO 527-2 | ||
| Yield, 90 ℃ | 3.7 | % | |
| Yield, 120 ℃ | 3.8 | % | |
| Yield, 150 ℃ | 4.1 | % | |
| Fracture, 23 ℃ | 2.2 | % | |
| Fracture, 60 ℃ | 2.6 | % | |
| Fracture, 90 ℃ | 4.2 | % | |
| Fracture, 120 ℃ | 4.2 | % | |
| Fracture, 150 ℃ | 4.7 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 7.0 | kJ/m² | |
| 23℃ | 10 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | 50 | kJ/m² | |
| 23℃ | 60 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 95 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 255 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 225 | ℃ | ISO 75-2/A |
| Continuous use temperature | 125 | ℃ | |
| Vicat Softening Temp | |||
| B50 | 240 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD：30~100℃ | 1.2E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | HB | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.0 mm | 960 | ℃ | |
| 2.0 mm | 960 | ℃ | |
| Extreme oxygen index | 26 | % | ASTM D2863 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Mold Shrinkage Pressure | 60.0 | MPa | ISO 294-4 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90.0 to 100 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 70.0 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |