| About |
|---|
| ULTEM™ AUT210 resin Transparent Polyetherimide (Tg 227 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 212 degC (SABIC IP method). Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).&&ULTEM™ AUT210 resin Transparent, Thermoplastic Polyimide (TPI). Glass transition Temperature (Tg) of 227degC. Haze onset temperature of 212degC (SABIC IP method). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Resin is a Dual-use item and is subject to export control restrictions under both U.S. 15 CFR , 774 and Annex I of Reg. (EC) 428/2009 as ECN 1C008. Diversion contrary to law is prohibited.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Low odor |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ASTM D792 |
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 337℃，6.60kg | 11 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 360℃，5 kg | 16.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.0 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3590 | MPa | ASTM D638 |
| Tensile modulus | 3320 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 88.0 | MPa | ASTM D638 |
| fracture | 88.0 | MPa | ISO 527-2/5 |
| yield | 105 | MPa | ASTM D638 |
| yield | 103 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 54 | % | ISO 527-2/5 |
| fracture | 75 | % | ASTM D638 |
| yield | 8.0 | % | ASTM D638 |
| yield | 7.0 | % | ISO 527-2/5 |
| Bending modulus | 3140 | MPa | ISO 178 |
| 50 mm span | 3330 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 170 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 16 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 38 | J/m | ASTM D256 |
| 23℃ | 37 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 2400 | J/m | ASTM D4812 |
| -30℃ | 4.0 | kJ/m² | ISO 180-1A |
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | No Break | ISO 180/1U | |
| 23℃ | No Break | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 33.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 100 mm span | 196 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 3.2 mm | 215 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 201 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 211 | ℃ | ASTM D648 |
| Vicat Softening Temp | 222 | ℃ | ASTM D1525 9 |
| B50 | 221 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：23~150℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~150℃ | 5.0E-5 | 1/℃ | ASTM E831 |
| MD：23~150℃ | 5.0E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~150℃ | 5.0E-5 | 1/℃ | ASTM E831 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Metallized Haze Onset | 212 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 24 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 60 | % | |
| Barrel rear temperature | 360 to 382 | °C | |
| Barrel middle temperature | 371 to 393 | °C | |
| Barrel front temperature | 382 to 404 | °C | |
| Nozzle temperature | 377 to 399 | °C | |
| Processing (melt) temperature | 382 to 404 | °C | |
| Mold temperature | 135 to 163 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |