| Haysite Plastics HCR-197 is a Thermoset Polyester product. It is available in North America. Characteristics include: Chemical Resistant Corrosion Resistant&& |
| Product Description | |
|---|---|
| Generic | 热固性聚酯 |
| Material Status | Commercial: Active |
| Features | Corrosion Resistant,Solvent resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| balance | 0.20 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 530 | J/m | ASTM D256 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| In air/in oil | 54000 | V | ASTM D149 |
| In air/in oil | 16 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Resistance | ASTM D229 | ||
| Burning Time | 5.0 | min | ASTM D229 |
| Ignition time | 1.4 | min | ASTM D229 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Babbitt hardness | 56 | ||
| tensile strength | 68.9 | MPa | ASTM D638 |
| bending strength | 152 | MPa | ASTM D790 |
| compressive strength | 207 | MPa | ASTM D695 |
| shear strength | 89.6 | MPa | ASTM D229 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Lengthwise |
| 3. Flatwise |
| 4. Perpendicular |
| 5. Parallel |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |