| About |
|---|
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | TPEE |
| Material Status | Commercial: Active |
| Features | High liquidity,Good Hardness,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | D792 |
| Melt Flow Rate | |||
| 220℃，2.16Kg | 8 | g/10min | D1238 |
| hardness | |||
| Maximum hardness | 37 | ISO868 | |
| 15 sec | 33 | ISO868 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| D-level | 40 | D2240 | |
| tensile strength | |||
| 10% strain | 3.4 | MPa | D638 |
| 5% strain | 2.2 | MPa | D638 |
| fracture | 25 | MPa | D638 |
| Tensile strain | |||
| fracture | 670 | % | D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | |||
| DSC | 191 | ℃ | D3418 |
| Process Conditions | |||
|---|---|---|---|
| Demoulding conditions | Nominal value | Unit | Test method |
| Injection conditions | Nominal value | Unit | Test method |
| Front barrel temperature | 210-215 | ℃ | |
| Middle temperature | 205-210 | ℃ | |
| Rear temperature | 190-195 | ℃ | |
| Hard mold temperature | 210-215 | ℃ | |
| Melt Temperature | 215-220 | ℃ | |
| Front barrel temperature | 210-215 | ℃ | |
| Middle temperature | 210-215 | ℃ | |
| Rear temperature | 205-210 | ℃ | |
| Nozzle temperature | 215-220 | ℃ | |
| Mold temperature | 35 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |